112-BuildWell Ready-Mix Plaster

112-BuildWell Ready-Mix Plaster
112-BuildWell Ready-Mix Plaster
Price And Quantity
  • 1
  • Ton/Tons
  • 10000.00 - 16000.00 INR
Product Specifications
  • Tanks, Walls, RoofsT
  • Putty
  • 20 kg and 40 kg bags
  • Construction
  • Good quality ,UV resistant, scratch resistant, water resistant, strong bonding, anti fungal and long lasting performancesand easy to use
Product Description

112-BuildWell Ready-Mix Plaster is manufactured by making use of premium grade materials under our modern dry mix plant with the help of computerized batch processes. It is a ready to use plaster with properties like excellent workability, longer durability and less rebounding losses. It provides a hard and smooth surface to the wall, column and ceiling. Also, it is resistant against rain water and several other adverse atmospheric conditions. 112-BuildWell Ready-Mix Plaster is crack free and also minimize the inconvenience of maintenance.  

Export Market : Worldwide

Feature

  • Compact plaster, reduce void gaps
  • Negligible silt content
  • Reduces rebounding
  • BuildWell Ready-Mix Plaster provides highly durable plaster that cuts repair the maintenance cost
  • Excellent work ability and good adhesion on various substrate
  • Paint finish and life of paint are enhanced

Technical specifications

TEST

TEST METHODS

SPECIFICATION

SETTING TIME: Initial

IS: 4031 PART - 5: 1988

>=30 min

SETTING TIME: Final

IS: 4031 PART - 5: 1988

<=600 min

PULL OFF ADHESION: 10mm thick on concrete. Storage 7 days in polythene bag @23°C + 7 days @ 23° C with 50% R.H.

ASTM 4541 & EN 1015-12

Min 0.3 Mpa

WATER RETENTIVITY

EN 1015-8

Min 95%

COMPRESSIVE STRENGTH:

EN 1015- 11:1999

As per EN 998 - 1 for categories (N/MM2)

2 day in mould + 5days in polythene bag + 21 days @23 degree C with 50% R.H.


CS I - 0.4 TO 2.5



CS II - 1.5 TO 5



CS lll - 3.5 TO 7.5



CS IV - >6+



Polymers already added, results in overall durability

FLEXURAL STRENGTH:

EN 1015- 11:1999

Min 1.8 Mpa

2 days in mould + 5 days in polythene bag + 21 days @23° C with 50 % R.H.



CAPILLARY WATER ABSORPTION

EN 1015- 18

As per EN 998 – 1



WO no requirements



W1 C <= 0.40 kg/m2.min0.5



W2 C <= 0.20 kg/m2.min0.5

Technical Details

PERFORMANCE PARAMETERS

JOB-SITE PLASTER

BuildWell Ready-Mix Plaster (RMP)

PENETRATION OF RAIN WATER

Large particle sizes (>3 mm) sand leads to porous surface and gives easy access to rainwater.

Different grade of sand used in exact proportion ensuring compactness in plaster.

ADHESION

High silt and chloride content in sand impedes adhesion properties in mortar, causing high de-bonding losses.

Negligible silt and organic matter free plaster ensure strong adhesion and durability.

DE-BONDING LOSSES

High

Negligible

SMOOTHNESS

Not so smooth

Smooth and hard surface provides aesthetic base of plaster to work upon.

CRACK FORMATION

Due to practical on site mixing practice, chances of crack formation is more.

(RMP) produced at automated dry mix plant. Chances of is very negligible subjected to proper curing and application.

WATER: CEMENT RATIO

Due to presence of moisture in sand it is not possible to determine exact quantity of water to be mixed.

Due to dry sand used, water cement ratio is easily maintained and full strength of plaster is obtained.

GRADING OF SAND

No grading

(RMP) has graded sand which results compactness of plaster.

CEMENT: SAND RATIO

Mistake may occur at job site mix

Sand cement ratio is maintained as (RMP) is made in automated plant.

PLASTER THICKNESS

Reducing of plaster is not possible.

Can be reduced up to 25% keeping the required strength.

POLYMER MODIFICATION

Polymer modification difficult as it involves multiple polymers and doses

Polymers already added, results in overall durability


Trade Information
  • 1000 Per Week
  • 1-7 Days
  • Plastic bags
  • All India
    Contact Us

    Rainbow Building, Plot No. 13, Sector-24, Turbhe, Navi Mumbai, Maharashtra, 400705, India
    Phone :+918045478697